saturation magnetization

The Curie's temperature Tc and saturation magnetization decreased obviously by Sr substituted with Cu or Ag and Sr2+ vacancy in the samples, while the initial susceptibility is increased.

通过用Cu或Ag部分替代Sr和少量Sr空位，使样品的居里温度和比饱和磁化强度比替代前的La（0.67）Sr（0.33）MnO3材料显著降低，而起始磁化率反而增加。

The Curie temperature and saturation magnetization of manganese-zinc ferrite were measured by using the electric bridge method, induced method and vibrating sample magnetometer ( VCM).

分别用电桥法、感应法和振动样品磁强计对锰锌铁氧体的居里温度和饱和磁化强度进行了测试。

Biaxial stress of ferromagnetic materials and residual stress of welding components have been measured by using the relation between Barkhausen effeet based on the law of approach to saturation magnetization and internal stress.

利用该技术，以近饱和磁化产生的巴克豪森效应与应力的关系，测量了铁磁构件的二轴应力和焊接构件的残余应力。

Mn-Zn ferrite nanoparticles are prepared by citrate auto-combustion method. Some researches have been made on effects of heat treatment temperature on coercivity and saturation magnetization of Mn-Zn ferrite nanoparticles.

采用柠檬酸盐自燃烧法制备纳米锰锌（Mn-Zn）铁氧体微粒，研究后续热处理温度对产物的饱和磁化强度（Ms）、矫顽力（Hc）的影响。

The Curie temperature and saturation magnetization increase with the Fe content.

居里温度和饱和磁化强度都随着Fe含量的增加而增高.

It is noteworthy that the saturation magnetization per Fe atom increased with increasing Fe concentration.

饱和磁化强度随掺杂浓度的增大而增大.

About the static magnetic property, with the temperature increasing, the saturation magnetization increased, at first increasing obviously, and then increasing slowly;

从静磁特性看，样品的饱和磁化强度随着还原温度的升高而增大，开始增加明显，后缓慢增加；

Ferrite is widely used as non-metallic magnetic materials in the area of high-frequency and light current. The poor magnetic energy stored per unit volume and low magnetic saturation magnetization limit the use in the domain of the low-frequency electric and high-power fields.

铁氧体是一种在高频弱电领域用途广泛的非金属磁性材料，但因单位体积中储存的磁能和饱和磁化强度较低，限制了它在高磁能密度的低频强电和大功率领域的应用。

The results of vibrating sample magnetometer ( VSM) experiment proved the ferromagnetic properties of Fe-doped ZnO at room temperature. The saturation magnetization, observed in this M-H curve, was around 10-3 emu and the coercivity of samples was 30 Oe.

磁性测量表明，ZnO∶Fe薄膜在室温下具有铁磁性，饱和磁化强度约为10-3emu量级，矫顽力为30奥斯特（Oe）。

Measuring Biaxial Stress of Ferromagnetic Materials by Using Barkhausen Effect Based on the Law of Approach to Saturation Magnetization

利用近饱和磁化产生的巴克豪森效应测量铁磁件二轴应力

In this paper the temperature dependent of saturation magnetization of titanium-substituted lithium ferrites has been theoretically calculated, then microwave ferrite materials with excellent performance have been made through controlling Fe content, adding Ca and V, and annealing in high-pressure oxygen.

对钛置换锂铁氧体进行了理论计算，在此基础上通过控制Fe含量，添加Ca、V离子及高压氧气退火等工艺，制备出了性能优良的微波铁氧体材料。

The stress-impedance effect can be improved by using metal layer with high conductivity and magnetic layer with high saturation magnetization.

提高中间金属层的电导率也可以提高应力阻抗效应。铁磁层采用高饱和磁化强度的材料可以增加多层膜的应力阻抗效应。

Scientists have been devoting to enhance the density of magnetic recording media for years. Magnetic materials are expected to be with high coercivity and high saturation magnetization.

提高磁记录介质的密度是人们多年所追求的目标，这要求磁性材料具有高矫顽力和相应的高饱和磁化强度。

Study on the Measurement Methods of Curie Temperature and Saturation Magnetization

居里温度和饱和磁化强度测量方法的研究

Study of saturation magnetization and coercive force of Ti ( CN) base cermets

Ti（CN）基金属陶瓷饱和磁化强度和矫顽磁力的研究

Temperature dependence of saturation magnetization and effective magnetic anisotropy of fe_ ( 83) nb_6b_ ( 11) alloy

Fe（83）Nb6B（11）合金的饱和磁化强度和有效各向异性

The experimental results show that saturation magnetization ss increases at the beginning and then decreases slowly, while coercive strength Hc decreases monotonously with increasing x, which is very beneficial to high-density magnetic recording.

实验结果表明，随替代量x的增大，比饱和磁化强度ss先增大后缓慢下降，而矫顽力Hc单调减小，这非常有利于用作高密度磁记录材料。